    How to detect the sealing performance of insulating glass

    Nov 2018

    1.The initial dew point/frost point is not enough, indicating that the residual moisture in the hollow glass air layer is saturated at -40 ° C; if the insulating glass reaches the initial dew point at higher temperature conditions, then it is possible to have an insulating glass sealing structure. A gap has occurred. In this case, there are many cases on the insulating glass made of composite strips.

     

    2. The vacuum box test can not pass, indicating that the sealing of the insulating glass has a gap, so that the hollow glass does not undergo external deflection under vacuum. This situation often occurs in the case of poor manual quality.

     

    3. The ultraviolet irradiation fails, and an oil film formed by cooling the volatile organic surface gas appears on the inner wall of the glass in the hollow glass air layer. It is indicated that the desiccant in the hollow glass cannot effectively adsorb the volatile organic solvent in the air layer. In this case, it is easy to appear on the insulating glass made of polysulfide rubber single-pass seal and using 3A or 4A molecular sieve desiccant.

     

    4. Failure of high temperature and high humidity test indicates that there is water condensation in the air layer of the insulating glass, which is caused by the fact that the insulating glass sealant does not effectively prevent external moisture from entering the hollow glass air layer. In this case, it is easy to appear on the insulating glass which is sealed by a single pass of polysulfide rubber

     

    5. Failure of the climate cycle test indicates that there is water condensation in the air layer of the insulating glass. The reason is that the insulating glass sealant does not effectively prevent external moisture from entering the hollow glass air layer. This situation often occurs on insulating glass made of composite strips.